Stainless Steel Welding Electrodes
Stainless Steel Welding Electrodes - 316L and 308L
316L and 308L are favorable class of stainless steel electrode/rod with best welding attributes. These multifunctional rutile rods are for binding less carbon austenitic acid retardant stainless steel sets like 316L and AISI 316. They are general in applications but normally for all industries, where superlative resistance again erosion is significant: Paper Mills, food Industry, Textile Industry, Chemical Industry etc. Further, the are effectively resistant against intergranular rust (till up to 400°C) and hot cracking. Minimum for 2 hours, re-dry it at 300o C. 312 is distinct electrode utilized to attache unalloyed steel or low alloyed to stainless, etc or where ever precised grade are not described.
Leveraging on TQM and word class infrastructure facility, we are engaged in manufacturing and exporting Stainless Steel Welding Electrodes. We source supreme quality stainless steels from reliable vendor base for manufacturing these electrodes as per industrial standards. Widely used in diverse areas for welding purposes, these electrodes are highly demanded among our clients due to their low hydrogen content, impeccable performance and light weight. Clients can get Stainless Steel Welding Electrodes at feasible prices.
| || |
|316L630||1/16” x 10” - 5# Box|
|316L650||3/32” x 12” - 10# Box|
|316L660||1/8” x 14” - 10# Box|
|316L670||5/32” x 14” - 10# Box|
|316L680||3/16" x 14" - 10# Box|
With firm commitment to quality, our organization is manufacturing and exporting a premium quality of Stainless Steel Welding Electrodes. Electrode is a terminal which helps in passing current from non metallic and metallic parts of an electric current. Offered electrodes are durable and powerful in nature that are widely used in welding stainless steel. Our manufactured Stainless Steel Welding Electrodes have low hydrogen content. Moreover, our electrodes are known for their dimensional accuracy, high performance and corrosion resistance.
- FULL LENGTH welding No red hotness and No wastages.
- Make Smooth Welding with self releasing slag & spatter.
- Low amperage and low heat input welding with Super thin sheet metal
- Less moisture absorption - No porosities, blow holes and rework.
- Best smooth welding and finely rippled weld beads.
- Best in class colour matching.
- Perfect re-striking.
- No chromium loss due to overheating
- Best in class vacuum packaging-minimum in-transit breakages. No wastages.
- Best in Class Packaging.
- Best in Class Mechanical Properties.
- Self Peeling Slag.
- Excellent Crack Resistant.
- Best Suitable in Pipe Welding.
|Chemical Composition of Deposited Metal(%)|
|Tensile Strength Rm(Mpa)||Elongation A4(%)|
|≥ 520||≥ 35|
The soldering rod identification solution for stainless steel curved binding is setup as mentioned below:
- E specify rod for arch welding.
- The foremost three numbers depicts American steel and iron kind of stainless steel whereas the last two numbers show the position and current used.
- The number E-308-16 in system stipulate institute of stainless steel kind 308, which is used in all places with consequent or reverse polarity straight current.
The covering of soldering rods for binding low and mild mixed alloy steels might have from 6 to 12 components, which comprises:
Cellulose to cater a gaseous protection with diminishing agent in which the air guard surrounding the curve is created by the fragmentation of cellulose.
metal carbonates to fix the base of slag and to cater shortening atmosphere.
Titanium dioxide to facilitate sort a topmost fluid but instant-freezing cinder as well as to supply ionization for the bend.
Ferrosilicon and ferromanganese to aid deoxidize the flowing weld metal and to add silicon and manganese content of the gathered weld metal.
Gums and Clays to proffer flexibility for extruding the coated plastic materials and also to provide strength to the layering.
Calcium Fluoride to serve covering gas to save the arc, alter basicity of clinker, which caters solubility and fluidity of metal oxides.
Mineral Silicates to render cinder that provide power to the electrode coating.
Alloy metal comprising molybdenum, chromium and nickel to give alloy substance to the gathered weld metal.
oxides of manganese or iron to modify the properties and fluidity of slag in order to facilitate balance the arc.
Iron powder to rise the productivity by catering more metal to be accumulated in the weld.
Arc untainted steel soldering electrodes have a explicit make-up on which a covering has been smeared by extrusion or dipping. The rods are created in three classic kinds with, mineral coating, cellulose coating and amalgamated coating of both cellulose and mineral.
The cellulose covering is constitute of dissolved cotton or various other forms of cellulose along with little amount of sodium, titanium or potassium. In some instances minerals are also added.
The mineral coating includes of metallic oxides clay, sodium silicate and different inorganic combinations or substances.
Electrodes covered with cellulose shield the liquid metal with aeriform area near the weld zone as well as arc. Whereas rods coated with mineral forms a cinder deposit. The bend untainted steel binding rods are utilized for cast iron, hard surfacing and welding steels.